Colombo, D.A.; Massone, J.M.; Echeverría, M.D.; Márquez, A.B."Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition" (2017) Ceramics International. 43(5):4263-4271
Estamos trabajando para incorporar este artículo al repositorio
Consulte el artículo en la página del editor
Consulte la política de Acceso Abierto del editor

Abstract:

This work studies the rolling contact fatigue (RCF) behavior of austempered ductile iron samples coated with Ti/TiN by cathodic arc deposition. The influence of the TiN layer thickness on the characteristics and RCF life of the coated samples is analyzed. RCF tests were performed in a flat washer type testing rig, using a thrust ball bearing as a counterpart. The maximum contact pressure was 1400 MPa. RCF tests results were analyzed using the two-parameter Weibull distribution. The rolling track of the tested samples was examined by using SEM and EDS. The results show that the surface hardness, residual stresses and coating adhesion strength of the samples increase as TiN layer thickness increases while surface roughness, coating hardness and elastic modulus do not vary significantly with the TiN layer thickness. Regarding the RCF tests, two failure mechanisms were observed in the coated samples, coating delamination and substrate spalling. Coating delamination turned out to be the most predominant mechanism and occurred at fewer loading cycles than substrate spalling. The EDS analysis revealed that inside the delaminated areas the Ti interlayer remained adhered to the substrates in all the cases. Extended tests on delaminated samples show growing delamination until final failure by substrate spalling occurred. The Weibull analysis indicates that the RCF life of the coated samples seems to have a tendency to increase with the TiN layer thickness and, in the case of the thicker TiN layer, to exceed the life of uncoated ADI after the extended tests. However, due to the number of samples employed, the statistic analysis does not show significant differences in the RCF behavior of the uncoated and coated samples. © 2016 Elsevier Ltd and Techna Group S.r.l.

Registro:

Documento: Artículo
Título:Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition
Autor:Colombo, D.A.; Massone, J.M.; Echeverría, M.D.; Márquez, A.B.
Filiación:Instituto de Investigaciones en Ciencia y Tecnología de Materiales, UNMdP, CONICET, Facultad de Ingeniería, Av. J. B. Justo 4302, Mar del Plata, B7608FDQ, Argentina
Instituto de Física del Plasma, UBA, CONICET, Departamento de Física, FCEyN, Intendente Güiraldes 2160 Pabellón I PB Ciudad Universitaria, Ciudad de Buenos Aires, C1428EGA, Argentina
Palabras clave:Austempered ductile iron; Cathodic arc deposition; Physical vapor deposition; Rolling contact fatigue; Ti interlayer; TiN; Ball bearings; Coatings; Delamination; Deposition; Ductility; Friction; Hardness; Physical vapor deposition; Spalling; Substrates; Surface roughness; Tin; Titanium compounds; Vapor deposition; Weibull distribution; Austempered ductile irons; Cathodic arc deposition; Coating delamination; Contact pressures; Failure mechanism; Rolling contact fatigue; Statistic analysis; Ti interlayers; Titanium nitride
Año:2017
Volumen:43
Número:5
Página de inicio:4263
Página de fin:4271
DOI: http://dx.doi.org/10.1016/j.ceramint.2016.12.068
Handle:http://hdl.handle.net/20.500.12110/paper_02728842_v43_n5_p4263_Colombo
Título revista:Ceramics International
Título revista abreviado:Ceram Int
ISSN:02728842
CODEN:CINND
Registro:https://bibliotecadigital.exactas.uba.ar/collection/paper/document/paper_02728842_v43_n5_p4263_Colombo

Referencias:

  • Dommarco, R.C., Bastias, P.C., Dall'O, H.A., Hahn, G.T., Rubin, C.A., Rolling Contact Fatigue (RCF) resistance of Austempered Ductile Iron (ADI) (1998) Wear, 221, pp. 69-74
  • Magalhães, L., Seabra, J., Sá, C., Experimental observations of contact fatigue crack mechanisms for austempered ductile iron (ADI) discs (2000) Wear, 246, pp. 134-148
  • Dommarco, R.C., Salvande, J.D., Contact fatigue resistance of austempered and partially chilled ductile irons (2003) Wear, 254, pp. 230-236
  • Dommarco, R.C., Jaureguiberry, A.J., Sikora, J.A., Rolling contact fatigue resistance of ductile iron with different nodule counts and matrix microstructures (2006) Wear, 261, pp. 172-179
  • Brunetti, C., Leite, M.V., Pintaude, G., Effect of specimen preparation on contact fatigue wear resistance of austempered ductile cast iron (2007) Wear, 263, pp. 663-668
  • Colombo, D.A., Echeverría, M.D., Laino, S., Dommarco, R.C., Massone, J.M., Rolling contact fatigue resistance of PVD CrN and TiN coated austempered ductile iron (2013) Wear, 308, pp. 35-45
  • Colombo, D.A., Echeverría, M.D., Dommarco, R.C., Massone, J.M., Influence of TiN coating thickness on the rolling contact fatigue resistance of austempered ductile iron (2016) Wear, 350-351, pp. 82-88
  • Krishna, D.S.R., Sun, Y., Chen, Z., Magnetron sputtered TiO2 films on a stainless steel substrate: selective rutile phase formation and its tribological and anti-corrosion performance (2011) Thin Solid Films, 519, pp. 4860-4864
  • Hong, Y.S., Kwon, S.H., Wang, T., Kim, D.-I., Choi, J., Kim, K.H., Effects of Cr interlayer on mechanical and tribological properties of Cr-Al-Si-N nanocomposite coating (2011) Trans. Nonferrous Met. Soc. China, 21, pp. s62-s67
  • Fontalvo, G.A., Daniel, R., Mitterer, C., Interlayer thickness influence on the tribological response of bi-layer coatings (2010) Tribol. Int., 43, pp. 108-112
  • Tang, J., Feng, L., Zabinski, J.S., The effects of metal interlayer insertion on the friction, wear and adhesion of TiC coatings (1998) Surf. Coat. Technol., 99, pp. 242-247
  • Borawski, B., Todd, J.A., Singh, J., Wolfe, D.E., The influence of ductile interlayer material on the particle erosion resistance of multilayered TiN based coatings (2011) Wear, 271, pp. 2890-2898
  • Bull, S.J., Jones, A.M., Multilayer coatings for improved performance (1996) Surf. Coat. Technol., 78, pp. 173-184
  • Diao, D.F., Sawaki, Y., Suzuki, H., Effect of interlayer on maximum contact stresses of hard coating under sliding contact (1996) Surf. Coat. Technol., 86-87, pp. 480-485
  • Shieu, F.S., Cheng, L.H., Shiao, M.H., Lin, S.H., Effects of Ti interlayer on the microstructure of ion-plated TiN coatings on AISI 304 stainless steel (1997) Thin Solid Films, 311, pp. 138-145
  • Colombo, D.A., Echeverría, M.D., Moncada, O.J., Massone, J.M., PVD TiN and CrN coated austempered ductile iron: analysis of processing parameters influence on coating characteristics and substrate microstructure (2012) ISIJ Int., 52, pp. 121-126
  • Fazio, M., Vega, D., Kleiman, A., Colombo, D., Franco Arias, L.M., Márquez, A., Study of the structure of titanium thin films deposited with a vacuum arc as a function of the thickness (2015) Thin Solid Films, 593, pp. 110-115
  • Martinschitz, K.J., Daniel, R., Mitterer, C., Keckes, J., Stress evolution in CrN/Cr coating systems during thermal straining (2008) Thin Solid Films, 516, pp. 1972-1976
  • Smithells, C.J., Brandes, E.A., (1976) Metals Reference Book, pp. 975-980. , 5th ed Butterworth London, UK
  • Zhang, M., He, J., Ab–initio calculation of elastic constants of TiN (2001) Surf. Coat. Technol., 142-144, pp. 125-131
  • Ou, Y.X., Lin, J., Tong, S., Sproul, W.D., Lei, M.K., Structure, adhesion and corrosion behavior of CrN/TiN superlattice coatings deposited by the combined deep oscillation magnetron sputtering and pulsed dc magnetron sputtering (2016) Surf. Coat. Technol., 293, pp. 21-27
  • Hamrock, B.J., Dowson, D., Isothermal Elastohydrodynamic Lubrication of Point Contacts: Part III - Fully Flooded Results (1977) J. Lubr. Technol., 99, pp. 264-275
  • Abernethy, R.B., (2000), Fourth ed. The New Weibull Handbook. R.B. Abernethy, North Palm Beach, Florida, USA; Vlcek, B.L., Zaretsky, E.V., Rolling-Element Fatigue Testing and Data Analysis—A Tutorial (2011) Tribol. Trans., 54, pp. 523-541
  • McCool, J.I., Using the Weibull Distribution: Reliability, Modeling and Inference (2012), Wiley Hoboken, New Yersey, USA; Chakraborty, J., Kumar, K., Ranjan, R., Chowdhury, S.G., Singh, S.R., Thickness-dependent fcc–hcp phase transformation in polycrystalline titanium thin films (2011) Acta Mater., 59, pp. 2615-2623
  • Roshanghias, A., Khatibi, G., Pelzer, R., Steinbrenner, J., On the effects of thickness on adhesion of TiW diffusion barrier coatings in silicon integrated circuits (2014) Surf. Coat. Technol., 259, pp. 386-392
  • Colombo, D.A., Echeverría, M.D., Moncada, O.J., Massone, J.M., Residual stress analysis in PVD coated austempered ductile iron (2013) ISIJ Int., 53, pp. 520-526
  • Tai, C.N., Koh, E.S., Akari, K., Macroparticles on TiN films prepared by the arc ion plating process (1990) Surf. Coat. Technol., 43-44, pp. 324-335
  • Colombo, D.A., Echeverría, M.D., Moncada, O.J., Massone, J.M., Characterisation of PVD–TiN coated austempered ductile iron: effects of nodule count and austempering temperature (2011) ISIJ Int., 51, pp. 448-455
  • Steinmann, P.A., Tardy, Y., Hintermann, H.E., Adhesion testing by the scratch test method: the influence of intrinsic and extrinsic parameters on the critical load (1987) Thin Solid Films, 154, pp. 333-349
  • Nie, X., Leyland, A., Song, H.W., Yerokhin, A.L., Dowey, S.J., Matthews, A., Thickness effects on the mechanical properties of micro-arc discharge oxide coatings on aluminium alloys (1999) Surf. Coat. Technol., 116-119, pp. 1055-1060
  • Chen, Y.-H., Polonsky, I.A., Chung, Y.-W., Keer, L.M., Tribological properties and rolling-contact-fatigue lives of TiN/SiNx multilayer coatings (2002) Surf. Coat. Technol., 154, pp. 152-161
  • Ahmed, R., Rolling contact fatigue (2002) ASM Handbook Volumen 11: failure analysis and prevention, pp. 941-956. , W.T. Becker R.J. Shipley ASM International, Materials Park Ohio, USA

Citas:

---------- APA ----------
Colombo, D.A., Massone, J.M., Echeverría, M.D. & Márquez, A.B. (2017) . Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition. Ceramics International, 43(5), 4263-4271.
http://dx.doi.org/10.1016/j.ceramint.2016.12.068
---------- CHICAGO ----------
Colombo, D.A., Massone, J.M., Echeverría, M.D., Márquez, A.B. "Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition" . Ceramics International 43, no. 5 (2017) : 4263-4271.
http://dx.doi.org/10.1016/j.ceramint.2016.12.068
---------- MLA ----------
Colombo, D.A., Massone, J.M., Echeverría, M.D., Márquez, A.B. "Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition" . Ceramics International, vol. 43, no. 5, 2017, pp. 4263-4271.
http://dx.doi.org/10.1016/j.ceramint.2016.12.068
---------- VANCOUVER ----------
Colombo, D.A., Massone, J.M., Echeverría, M.D., Márquez, A.B. Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition. Ceram Int. 2017;43(5):4263-4271.
http://dx.doi.org/10.1016/j.ceramint.2016.12.068