Abstract:
This work studies the surface characteristics and, particularly, the rolling contact fatigue (RCF) behavior of austempered ductile iron (ADI) samples coated with TiN based coatings of about 1 μm in thickness. Films synthesized by cathodic arc deposition (CAD) at a fixed nitrogen flow, compositional gradient films synthesized by CAD at a variable nitrogen flow and plasma based ion implanted and deposited (PBIID) films were comparatively analyzed. The results indicated that CAD films showed a strong TiN (111) preferred orientation while PBIID films a more randomly orientation. The crystallite size of CAD films was more than the double of PBIID films. Residual stresses of the PBIID films were lower than those of CAD films, the lowest hardness and elastic modulus were obtained for CAD films grown at variable nitrogen flow, while no significant differences in roughness, H/E ratio and adhesion were observed among the different films. Regarding RCF tests, failures in samples coated with TiN at constant flow were characterized by a progressive coating delamination followed by the formation of fatigue spalls inside the delaminated areas. Failures in samples coated with PBIID and gradient TiN were characterized by the formation of fatigue spalls with slight coating delamination. There were no significant differences between the RCF resistance of uncoated ADI and the samples with CAD films while the samples with PBIID films had a noticeably higher resistance. The better performance could be associated with the low compressive residual stresses and the fine grained microstructure induced by the PBIID process. © 2018 Elsevier B.V.
Registro:
Documento: |
Artículo
|
Título: | Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition |
Autor: | Quintana, J.P.; Massone, J.M.; Márquez, A.B.; Colombo, D.A. |
Filiación: | Universidad de Buenos Aires, Consejo Nacional de investigaciones Científicas y Técnicas, Instituto de Física del Plasma (INFIP), Facultad de Ciencias Exactas y Naturales, Intendente Güiraldes 2160 Pabellón I PB Ciudad Universitaria, CABA, C1428EGA, Argentina Universidad de Buenos Aires, Facultad de Ciencias Exactas y Naturales, Departamento de Física, Intendente Güiraldes 2160 Pabellón I PB Ciudad Universitaria, CABA, C1428EGA, Argentina Instituto de Investigaciones en Ciencia y Tecnología de Materiales, UNMdP, CONICET, Facultad de Ingeniería, Av. J. B. Justo 4302, Mar del Plata, B7608FDQ, Argentina
|
Palabras clave: | Austempered ductile iron; Cathodic arc deposition; Ion implantation; Rolling contact fatigue; Titanium nitride; Coatings; Crystallite size; Ductility; Friction; Ion implantation; Ions; Nitrogen; Nitrogen plasma; Physical vapor deposition; Residual stresses; Titanium nitride; Austempered ductile irons; Cathodic arc deposition; Compositional gradients; Compressive residual stress; Fine-grained microstructure; Hardness and elastic modulus; Plasma based ion implantation and deposition; Rolling contact fatigue; Fatigue of materials |
Año: | 2019
|
Volumen: | 671
|
Página de inicio: | 95
|
Página de fin: | 102
|
DOI: |
http://dx.doi.org/10.1016/j.tsf.2018.12.014 |
Título revista: | Thin Solid Films
|
Título revista abreviado: | Thin Solid Films
|
ISSN: | 00406090
|
CODEN: | THSFA
|
Registro: | https://bibliotecadigital.exactas.uba.ar/collection/paper/document/paper_00406090_v671_n_p95_Quintana |
Referencias:
- Dommarco, R.C., Bastias, P.C., Dall'O, H.A., Hahn, G.T., Rubin, C.A., Rolling contact fatigue (RCF) resistance of austempered ductile iron (ADI) (1998) Wear, 221, pp. 69-74
- Magalhães, L., Seabra, J., Sá, C., Experimental observations of contact fatigue crack mechanisms for austempered ductile iron (ADI) discs (2000) Wear, 246, pp. 134-148
- Dommarco, R.C., Salvande, J.D., Contact fatigue resistance of austempered and partially chilled ductile irons (2003) Wear, 254, pp. 230-236
- Dommarco, R.C., Jaureguiberry, A.J., Sikora, J.A., Rolling contact fatigue resistance of ductile iron with different nodule counts and matrix microstructures (2006) Wear, 261, pp. 172-179
- Brunetti, C., Leite, M.V., Pintaude, G., Effect of specimen preparation on contact fatigue wear resistance of austempered ductile cast iron (2007) Wear, 263, pp. 663-668
- Wang, B., He, M., Barber, G.C., Schall, J.D., Tao, C., Sun, X., Rolling contact fatigue resistance of austempered ductile iron processed at various austempering holding times (2018) Wear, 398-399, pp. 41-46
- Zammit, A., Abela, S., Michalczewski, R., Kalbarczyk, M., Wagner, L., Mhaede, M., Wan, R., Grech, M., Influence of shot peening on the rolling contact fatigue resistance of Cu-Ni austempered ductile iron (2014) Proceedings of the 12th International Conference on Shot Peening, Goslar, Germany, p. 68. , 15 September
- Feng, H.P., Lee, S.C., Hsu, C.H., Ho, J.M., Study of high cycle fatigue of PVD surface–modified austempered ductile iron (1999) Mater. Chem. Phys., 59, pp. 154-161
- Hsu, C.-H., Lu, J.-K., Lai, K.-L., Chen, M.-L., Erosion and corrosion behaviors of ADI deposited TiN/TiAlN coatings by cathodic arc evaporation (2005) Mater. Trans., 46, pp. 1417-1424
- Hsu, C.-H., Chen, K.-L., Lu, J.-H., Effects of electroless nickel interlayer on surface properties of CrN arc-coated austempered ductile iron (2008) Surf. Coat. Technol., 203, pp. 868-871
- Hsu, C.H., Lee, C.Y., Chen, K.L., Lu, J.H., Effects of CrN/EN and Cr2O3/EN duplex coatings on corrosion resistance of ADI (2009) Thin Solid Films, 517, pp. 5248-5252
- Hsu, C.H., Chen, K.L., Lu, K.C., Effects of low–temperature duplex coatings on the abrasive and erosive behavior of ADI (2011) Thin Solid Films, 519, pp. 4855-4859
- Hsu, C.-H., Huang, K.-H., Chen, Y.-T., Ho, W.-Y., The effect of electroless Ni–P interlayer on corrosion behavior of TiN-coated austempered ductile iron (2013) Thin Solid Films, 529, pp. 34-38
- Knotek, O., Atzor, M., Jungblut, F., Prengel, H.G., Wear resistance of arc-evaporated and magnetron-sputtered coatings on cemented carbides (1989) Surf. Coat. Technol., 39, pp. 445-453
- Han, J.G., Nam, K.H., Choi, I.S., The shear impact wear behavior of Ti compound coatings (1998) Wear, 214, pp. 91-97
- Björk, T., Westergård, R., Hogmark, S., Bergström, J., Hedenqvist, P., Physical vapour deposition duplex coatings for aluminium extrusion dies (1999) Wear, 225-229, pp. 1123-1130
- Lomello, F., Sanchette, F., Schuster, F., Tabarant, M., Billard, A., Influence of bias voltage on properties of AlCrN coatings prepared by cathodic arc deposition (2013) Surf. Coat. Technol., 224, pp. 77-81
- Lomello, F., Yazdi, M.A.P., Sanchette, F., Schuster, F., Tabarant, M., Billard, A., Temperature dependence of the residual stresses and mechanical properties in TiN/CrN nanolayered coatings processed by cathodic arc deposition (2014) Surf. Coat. Technol., 238, pp. 216-222
- Han, B., Pelenovich, V.O., Yousaf, M.I., Yan, S.J., Wang, W., Zhou, S.Y., Yang, B., Fu, D.J., Properties of CrN/Mo2N nano-multilayer films synthesized by multi-cathodic arc ion plating system (2016) Thin Solid Films, 619, pp. 160-165
- Lugscheider, E., Barimani, C., Wolff, C., Guerreiro, S., Doepper, G., Comparison of the structure of PVD-thin films deposited with different deposition energies (1996) Surf. Coat. Technol., 86, pp. 177-183
- Colombo, D.A., Echeverría, M.D., Dommarco, R.C., Massone, J.M., Influence of TiN coating thickness on the rolling contact fatigue resistance of austempered ductile iron (2016) Wear, 350-351, pp. 82-88
- Colombo, D.A., Echeverría, M.D., Laino, S., Dommarco, R.C., Massone, J.M., Rolling contact fatigue resistance of PVD CrN and TiN coated austempered ductile iron (2013) Wear, 308, pp. 35-45
- Colombo, D.A., Massone, J.M., Echeverría, M.D., Márquez, A.B., Rolling contact fatigue behavior of Ti/TiN coated ADI by cathodic arc deposition (2017) Ceram. Int., 43, pp. 4263-4271
- Colombo, D.A., Mandri, A.D., Echeverría, M.D., Massone, J.M., Dommarco, R.C., Mechanical and tribological behavior of Ti/TiN and TiAl/TiAlN coated austempered ductile iron (2018) Thin Solid Films, 647, pp. 19-25
- Naebe, M., Shirvanimoghaddam, K., Functionally graded materials: A review of fabrication and properties (2016) Appl. Mater. Today, 5, pp. 223-245
- Inoue, S., Ucihda, H., Takeshita, K., Koterazawa, K., Howson, R.P., Preparation of compositionally gradient Ti-TiN films by r.f. reactive sputtering (1995) Thin Solid Films, 261, pp. 115-119
- PalDey, S., Deevi, S.C., Properties of single layer and gradient (Ti,Al)N coatings (2003) Mater. Sci. Eng. A, 361, pp. 1-8
- Liu, T., Dong, C., Wu, S., Tang, K., Wang, J., Jia, J., TiN, TiN gradient and Ti/TiN multi-layer protective coatings on Uranium (2007) Surf. Coat. Technol., 201, pp. 6737-6741
- Gerstner, E.G., McKenzie, D.R., Adherent carbon film deposition by cathodic arc with implantation (1995) J. Vac. Sci. Technol. A, 13, pp. 406-411
- Tarrant, R.N., Montross, C.S., McKenzie, D.R., Combined deposition and implantation in the cathodic arc for thick film preparation (2001) Surf. Coat. Technol., 136, pp. 188-191
- Colombo, D.A., Echeverría, M.D., Moncada, O.J., Massone, J.M., Characterisation of PVD–TiN coated austempered ductile iron: effects of nodule count and austempering temperature (2011) ISIJ Int., 51, pp. 448-455
- Standard Test Method for Evaluating the Microstructure of Graphite in Iron Castings (2017), ASTM A247-17, ASTM International; Fazio, M., Vega, D., Kleiman, A., Colombo, D., Franco Arias, L.M., Márquez, A., Study of the structure of titanium thin films deposited with a vacuum arc as a function of the thickness (2015) Thin Solid Films, 593, pp. 110-115
- Smithells, C.J., Brandes, E.A., Metals Reference Book (1976), 5th ed. Butterworth London, UK; Zhang, M., He, J., Ab–initio calculation of elastic constants of TiN (2001) Surf. Coat. Technol., 142-144, pp. 125-131
- Holzwarth, U., Gibson, N., The Scherrer equation versus the ‘Debye-Scherrer equation’ (2011) Nat. Nanotechnol., 6, p. 534
- Ljungcrantz, H., Oden, M., Hultman, L., Greene, J.E., Sundgren, J.E., Nanoindentation studies of single-crystal (001)-, (011)-, and (111)-oriented TiN layers on MgO (1996) J. Appl. Phys., 80, pp. 6725-6733
- Heinke, W., Leyland, A., Matthews, A., Berg, G., Friedrich, C., Broszeit, E., Evaluation of PVD nitride coatings, using impact, scratch and Rockwell–C adhesion tests (1995) Thin Solid Films, 270, pp. 431-438
- Rolling Contact Fatigue Testing of Bearing Steels (1982), ASTM STP771, ASTM International; Johnson, K.L., Contact Mechanics (1987), Cambridge University Press Cambridge, UK; Hahn, G.T., Bhargava, V., Chen, Q., The cyclic stress-strain properties, hysteresis loop shape, and kinematic hardening of two high-strength bearing steels (1990) MTA, 21, pp. 653-665
- Hamrock, B.J., Dowson, D., Isothermal elastohydrodynamic lubrication of point contacts: part III - fully flooded results (1977) J. Lubr. Technol., 99, pp. 264-275
- Abernethy, R.B., The New Weibull Handbook, 4th Edition ed (2000), Florida, USA R.B. Abernethy; McCool, J.I., Using the Weibull Distribution: Reliability (2012), Modeling and Inference Wiley, New Yersey, USA; Rybiak, R., Fouvry, S., Liskiewicz, T., Wendler, B., Fretting wear of a TiN PVD coating under variable relative humidity conditions - development of a “composite” wear law (2008) Surf. Coat. Technol., 202, pp. 1753-1763
- Yoon, S.-Y., Kim, J.-K., Kim, K.H., A comparative study on tribological behavior of TiN and TiAlN coatings prepared by arc ion plating technique (2002) Surf. Coat. Technol., 161, pp. 237-242
- Vaz, F., Ferreira, J., Ribeiro, E., Rebouta, L., Lanceros-Méndez, S., Mendes, J.A., Alves, E., de Rijk, J., Influence of nitrogen content on the structural, mechanical and electrical properties of TiN thin films (2005) Surf. Coat. Technol., 191, pp. 317-323
- Shtansky, D.V., Kulinich, S.A., Levashov, E.A., Sheveiko, A.N., Kiriuhancev, F.V., Moore, J.J., Localized deformation of multicomponent thin films (2002) Thin Solid Films, 420-421, pp. 330-337
- Ljungcrantz, H., Hultman, L., Sundgren, J.E., Karlsson, L., Ion induced stress generation in arc-evaporated TiN films (1995) J. Appl. Phys., 78, pp. 832-837
- Odén, M., Almer, J., Håkansson, G., The effects of bias voltage and annealing on the microstructure and residual stress of arc-evaporated Cr–N coatings (1999) Surf. Coat. Technol., 120-121, pp. 272-276
- Christensen, C., On the origin of spherical particles found on fatigue fracture surfaces and ferrograms (1979) Wear, 53, pp. 189-193
- Loy, B., McCallum, R., Mode of formation of spherical particles in rolling contact fatigue (1973) Wear, 24, pp. 219-228
- Scott, D., Mills, G.H., Spherical debris—Its occurrence, formation and significance in rolling contact fatigue (1973) Wear, 24, pp. 235-242
- Liu, H., Jiang, Y., Zhou, R., Tang, B., Mechanical property and rolling contact fatigue life of TiN film on bearing steel by plasma immersion ion implantation and deposition (2013) Rev. Adv. Mater. Sci., 33, pp. 131-136
- Liu, H.X., Jiang, Y.H., Zhou, R., Li, Z.L., Tang, B.Y., Investigating the mechanical property and rolling contact fatigue life of diamond-like carbon films on bearing steel (2008) Mater. Sci. Forum, 575-578, pp. 990-995
- Liu, H., Tang, B., Wang, L., Wang, X., Jiang, B., Fatigue life and mechanical behaviors of bearing steel by nitrogen plasma immersion ion implantation (2007) Surf. Coat. Technol., 201, pp. 5273-5277
- Erdemir, A., Hochman, R.F., Surface metallurgical and tribological characteristics of TiN-coated bearing steels (1988) Surf. Coat. Technol., 36, pp. 755-763
- Polonsky, I.A., Chang, T.P., Keer, L.M., Sproul, W.D., An analysis of the effect of hard coatings on near-surface rolling contact fatigue initiation induced by surface roughness (1997) Wear, 208, pp. 204-219
Citas:
---------- APA ----------
Quintana, J.P., Massone, J.M., Márquez, A.B. & Colombo, D.A.
(2019)
. Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition. Thin Solid Films, 671, 95-102.
http://dx.doi.org/10.1016/j.tsf.2018.12.014---------- CHICAGO ----------
Quintana, J.P., Massone, J.M., Márquez, A.B., Colombo, D.A.
"Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition"
. Thin Solid Films 671
(2019) : 95-102.
http://dx.doi.org/10.1016/j.tsf.2018.12.014---------- MLA ----------
Quintana, J.P., Massone, J.M., Márquez, A.B., Colombo, D.A.
"Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition"
. Thin Solid Films, vol. 671, 2019, pp. 95-102.
http://dx.doi.org/10.1016/j.tsf.2018.12.014---------- VANCOUVER ----------
Quintana, J.P., Massone, J.M., Márquez, A.B., Colombo, D.A. Rolling contact fatigue behavior of TiN based coatings deposited on ADI by cathodic arc deposition and plasma based ion implantation and deposition. Thin Solid Films. 2019;671:95-102.
http://dx.doi.org/10.1016/j.tsf.2018.12.014