Abstract:
We report in situ successive depositions of nickel nanoparticles and carbon nanotubes (CNTs) on ordered mesoporous silica films used as template for the catalyst particles. The mesoporous films are synthesized by the evaporation-induced self-assembly process from tetraethyl orthosilicate derived oligomers and a di-block copolymer from dip-coating deposition method. The substrates are decorated with Ni nanoparticles through Ion Beam Deposition and posterior annealing to induce metal coalescence in the mesoporous cavities. CNTs were then grown by Chemical Vapor Deposition in the presence of an electric field. These techniques provide a simple control method producing ordered arrangements of catalyst nanoparticles and ordered nanostructures for large area applications. © 2010 Elsevier B.V. All rights reserved.
Registro:
Documento: |
Artículo
|
Título: | Nickel nanoparticles decoration of ordered mesoporous silica thin films for carbon nanotubes growth |
Autor: | Acuña, J.J.S.; Marchi, M.C.; Alvarez, F. |
Filiación: | Institute of Physics Gleb Wataghin, University of Campinas, UNICAMP, 13083-970, Campinas, SP, Brazil INQUIMAE-DQIAQF, Universidad de Buenos Aires, Facultad de Ciencias Exactas y Naturales, C1428EHA Buenos Aires, Argentina
|
Palabras clave: | Carbon nanotubes; Catalyst decoration; CVD; Mesoporous; Catalyst nanoparticle; Catalyst particles; CVD; Dip coating; Evaporation-induced self-assembly; In-situ; Ion beam deposition; Mesoporous; Mesoporous films; Ni Nanoparticles; Nickel nanoparticles; Ordered arrangement; Ordered mesoporous silica film; Ordered mesoporous silicas; Ordered nanostructures; Simple control method; Tetra-ethyl-ortho-silicate; Block copolymers; Carbon nanotubes; Catalysts; Chemical modification; Chemical vapor deposition; Coalescence; Electric fields; Mesoporous materials; Nanoparticles; Oligomers; Silica; Carbon films |
Año: | 2010
|
Volumen: | 519
|
Número: | 1
|
Página de inicio: | 214
|
Página de fin: | 217
|
DOI: |
http://dx.doi.org/10.1016/j.tsf.2010.07.119 |
Título revista: | Thin Solid Films
|
Título revista abreviado: | Thin Solid Films
|
ISSN: | 00406090
|
CODEN: | THSFA
|
Registro: | https://bibliotecadigital.exactas.uba.ar/collection/paper/document/paper_00406090_v519_n1_p214_Acuna |
Referencias:
- Gu, J.L., You, G.J., Shi, J.L., Xiong, L.M., Hua, Z.L., Chen, H.R., Qian, S.X., (2005) Adv. Mater., 17, p. 557
- Zhong, Z.Y., Lin, J.Y., Teh, S.P., Teo, J., Dautzenberg, F.M., (2007) Adv. Funct. Mater., 17, p. 1402
- Dresselhaus, M.S., Dresselhaus, G., Eklund, P.C., (1996) Science of Fullerenes and Carbon Nanotubes, , AP, Elsevier Science USA
- Robertson, J., (2007) Mater. Today, 10, p. 37
- Eres, G., Puretzty, A.A., Geohegan, D.B., Cui, H., (2004) Appl. Phys. Lett., 84, p. 1759
- Terrones, M., Charlier, J.C., Banhart, H., Grobert, N., Ajayan, P.M., (2002) New Diam. Front. Carbon Technol., 12, p. 315
- Tsung, C.K., Hong, W.B., Shi, Q.H., Kou, X.S., Yeung, M.H., Wang, J.F., Stucky, G.D., (2006) Adv. Funct. Mater., 16, p. 2225
- Gu, J., Fan, W., Shimojima, A., Okubo, T., (2008) J. Solid State Chem., 181, p. 957
- Bouchet-Fabre, B., Fadjie Djomkam, A., Delmas, M., Jin, C., Antonin, O., Hugon, M.C., Mayne-L'Hermite, M.F., Minéa, T., (2009) Carbon, 47, p. 3424
- Wan, Y., Yang, H.F., Zhao, D.Y., (2006) Acc. Chem. Res., 39, p. 423
- Marchi, M.C., Figueroa, C.A., Alvarez, F., (2008) J. Nanosci. Nanotechnol., 8, p. 448
- Gupta, G., Shah, P.S., Zhang, X.G., Saunders, A.E., Korgel, B.A., Johnston, K.P., (2005) Chem. Mater., 17, p. 6728
- Botella, P., Corma, A., Navarro, M.T., (2007) Chem. Mater., 19, p. 1979
- Asefa, T., Lennox, R.B., (2005) Chem. Mater., 17, p. 2481
- Gu, J.L., Shi, J.L., Xiong, L.M., Chen, H.R., Ruan, M.L., (2004) Microporous Mesoporous Mater., 74, p. 199
- Wang, L.Z., Shi, J.L., Zhang, W.H., Ruan, M.L., Yu, J., Yan, D.S., (1999) Chem. Mater., 11, p. 3015
- Huang, M.H., Choudrey, A., Yang, P.D., (2000) Chem. Commun., 12, p. 1063
- Kobayashi, K., Kitaura, R., Kumai, Y., Goto, Y., Inagaki, S., Shinohara, H., (2008) Chem. Phys. Lett., 458, p. 346
- Hernadi, K., Fonseca, A., Nagy, J.B., Bernaerts, D., Fudala, A., Lucas, A.A., (1996) Zeolites, 17, p. 416
- Mukhopadhyay, K., Koshio, A., Tanaka, N., Shinohara, H., (1998) Jpn. J. Appl. Phys., 37, p. 1257
- Okamoto, A., Kawakubo, T., Hiraoka, T., Okazaki, T., Sugai, T., Shinohara, H., (2002) Mol. Cryst. Liq. Cryst., 387, p. 317
- Wang, X., Li, Q., Xie, J., Jin, Z., Wang, J., Li, Y., Jiang, K., Fan, S., (2009) Nano Lett., 9, p. 3137
- Jiang, K.L., Li, Q., Fan, S., (2002) Nature, 419, p. 801
- Zhang, X.B., Jiang, K.L., Feng, C., Liu, P., Zhang, L.N., Kong, J., Zhang, T.H., Fan, S., (2006) Adv. Mater., 18, p. 1505
- Wu, Y., Yang, B., (2002) Nano Lett., 2, p. 355
- Zhang, Y., Chang, A., Cao, J., Wang, Q., Kim, W., Li, Y., Morris, N., Dai, H., (2001) Appl. Phys. Lett., 79, p. 3155
- Van Der Meer, J., Bardez, I., Bart, F., Albouy, P.-A., Wallez, G., Davidson, A., (2009) Microporous Mesoporous, 118, p. 183
- Ago, H., Imamura, S., Okazaki, T., Saito, T., Yumura, M., Tsuji, M., (2005) J. Phys. Chem. B, 109, p. 10035
- Mann, S., Burkett, S.L., Davis, S.A., Fowler, C.E., Mendelson, N.H., Sims, S.D., Walsh, D., Whilton, N., (1997) Chem. Mater., 9, p. 2300
- Ding, F., Rosén, A., Boltn, K., (2004) J. Chem. Phys., 121, p. 2775
- Raty, J.Y., Gygi, F., Galil, G., (2005) Phys. Rev. Lett., 95, p. 096103
- Brinker, C.J., Lu, Y., Sellinger, A., Fan, H., (1999) Adv. Mater., 11, p. 579
- Lu, Y., Fan, H., Stump, A., Ward, T.L., Rieker, T., Brinker, C.J., (1999) Nature, 398, p. 223
- Angelomé, P.C., Fuertes, M.C., Soler-Illia, G.J.A.A., (2006) Adv. Mater., 18, p. 2397
- Cagnol, F., Grosso, D., Soler-Illia, G.J.A.A., Crepaldi, E.L., Babonneau, F., Amenitsch, H., Sanchez, C., (2003) J. Mater. Chem., 13, p. 61
- Fuertes, M.C., Lopez-Alcaraz, F.J., Marchi, M.C., Troiani, H.E., Luca, V., Míguez, H., Soler-Illia, G.J.A.A., (2007) Adv. Funct. Mater., 17, p. 1247
- Chapman, B., (1980) Glow Discharge Process, , J. Wiley & Sons New York
- Helveg, S., Lopez-Cartes, C., Sehested, J., Hansen, P.L., Clausen, B.S., Rostrup-Nielsen, J.R., Abild-Pedersen, F., Norskov, J.K., (2004) Nature, 427, p. 426
- Hendrich, C., Favre, L., Ievlev, D.N., Dobrynin, A.N., Bras, W., Hörmann, U., Piscopiello, E., Temst, K., (2007) Appl. Phys., A Mater. Process., 86, p. 533
- Müller, J., Löthman, P., Meyer, D.C., (2005) Cryst. Res. Technol., 40, p. 177
Citas:
---------- APA ----------
Acuña, J.J.S., Marchi, M.C. & Alvarez, F.
(2010)
. Nickel nanoparticles decoration of ordered mesoporous silica thin films for carbon nanotubes growth. Thin Solid Films, 519(1), 214-217.
http://dx.doi.org/10.1016/j.tsf.2010.07.119---------- CHICAGO ----------
Acuña, J.J.S., Marchi, M.C., Alvarez, F.
"Nickel nanoparticles decoration of ordered mesoporous silica thin films for carbon nanotubes growth"
. Thin Solid Films 519, no. 1
(2010) : 214-217.
http://dx.doi.org/10.1016/j.tsf.2010.07.119---------- MLA ----------
Acuña, J.J.S., Marchi, M.C., Alvarez, F.
"Nickel nanoparticles decoration of ordered mesoporous silica thin films for carbon nanotubes growth"
. Thin Solid Films, vol. 519, no. 1, 2010, pp. 214-217.
http://dx.doi.org/10.1016/j.tsf.2010.07.119---------- VANCOUVER ----------
Acuña, J.J.S., Marchi, M.C., Alvarez, F. Nickel nanoparticles decoration of ordered mesoporous silica thin films for carbon nanotubes growth. Thin Solid Films. 2010;519(1):214-217.
http://dx.doi.org/10.1016/j.tsf.2010.07.119